Uralplastic film with Appeel®
Background
Objectives:
1/ Adhesion strength
2/ thickness measure of the film with Appeel®72D811
2/ IR identification of the film with Appeel®72D811
Summary
620.00K
Category: advertisingadvertising

Uralplastic film with Appeel®

1. Uralplastic film with Appeel®

Results of Analysis
Mariane Zebri
Cedric Thomi
P&IP

2. Background

2
Background
Following the visit at Uralplastic the 18th of February, I came back with
3 samples:
1/. Peel to PS: they used for this 3 Appeel® grade 11D554, 20D855 and
20D751, they didn’t have a good peel at 170-180°C and the peeling is
not stable. Generally the structure is: 20% / 50% / 30%
(Appeel®:10microns)
2/. Second point of discussion the Appeel®72D811, they are looking
for something for PET/Pe and PVC/PE trays, they have produced a
film of Appeel®72D811 with 3% of Conpol 20S2 and 2% of Conpol 20B.
We will performe some analysis on this one.
3/. Others topics: Appeel®93D894 and also tie layer in presence of AF
recommandation Bynel®4109, proposition of used of Surlyn 1605 to
avoid leackers on the corner of trays.

3. Objectives:

3
Objectives:
1/ For the 2 structures with Appeel®20D855 and Appeeel®11D554,
measure the adhesion strenght on PS between 160 to 210°C.
2/ For the structure with Appeeel®72D811, the analysis will be the
control of the thickness of each layer and also the measure of peeling
on PE between 120 and 180°C.

4. 1/ Adhesion strength

4
1/ Adhesion strength
Sealing temperatures*
onto PS
Values in N/15mm
Structure with
160°C
180°C
200°C
220°C
Appeel® 11D554
7.4
8.8
9.4
11.6
Appeel® 20D855
6.1
Break
Break
Break
With the Appeel® 20D855 after 160°C , the film Break so the adhesion
strength is higher than the film strength itself.
2/ Adhesion strength of Appeel®72D811
Sealing temperatures*
onto LDPE
Values in N/15mm
Structure with
120°C
140°C
160°C
180°C
Appeel® 71D811
0.2
4
4.3
4.7
* Heat sealed with upper bar only (Brugger equipment, 0.3MPa, 1sec)

5. 2/ thickness measure of the film with Appeel®72D811

5
2/ thickness measure of the film with
Appeel®72D811

6. 2/ IR identification of the film with Appeel®72D811

6
2/ IR identification of the film with Appeel®72D811
PE in one side
Appeel®72D811
On the other side

7. Summary

7
Summary
For the Appeel® 11D554 and 20D855, we observe that the adhesion is very high
for the 20D855.
And for the third film with Appeel®72D811, we confirm the structure and thisckness,
and also the adhesion on PE was perfomed.